name:HT - Cu75 copper agent

time:2018-11-3 15:06:55


Introduction
I. purpose:
Adjust the content of copper in different aluminum alloy to replace the intermediate alloy, which can reduce the melting temperature.
Ⅱ. Product features:
1. Element content 75%
2. The yield is greater than 95%
3. Direct input, easy to use.
Ⅲ. Usage:
According to the production of alloy element content in the alloy and the results of the analysis before furnace, calculated at 90% recovery efficiency may be additive quantity (Cu) after grilled slag, uniform aluminum points and thrown into the molten pool directly, after being small flame disappeared, should be appropriate to strengthen artificial stirring, make its spread evenly, and according to the actual situation, the spread of the guarantee time.
Ⅳ. Process parameters:
1, using temperature: 740-760 ℃
2. Amount of addition (kg) = (alloy element composition (%) - pre-furnace analysis of the element content)
3. Melting time: 15-30 minutes
Ⅴ. packaging and storage:
Each box is 25kg and stored in dry place for 6 months.
Of the goods
model
use
Method of use
The characteristics of
The process parameters
specifications
Titanium boron agent
HT - Ti4OB4
Adjust the composition of alloying elements to replace the aluminum intermediate alloy.
According to the production of alloy element content in the alloy and the results of the analysis before furnace, calculated at 95% of the recovery efficiency is good, need to add dose, after grilled slag, aluminum evenly dispersed bubble into the molten pool directly, after being small flame disappeared, should be appropriate to strengthen artificial stirring, make its spread evenly, and according to the actual situation, the spread of the guarantee time.
The elements are 75% and the silicon is 95%.
The yield is greater than 95%.
The solid yield of iron agent is over 90%.
Shelf life is one year.
Temperature: 740 ℃ to 760 ℃.
Melt time: 15 to 30 minutes.
1, 500 g/piece
Density: 3.8-4.2 kg/cm after
Si: 2.5 g/cm after
Titanium agent
HT - Ti75
Manganese agent
HT - Mn75
Copper agent
HT - Cu75
iron
HT - Fe75
Chromium agent
HT - Cr75
Nickel agent
HT - Ni75
zinc
HT - Zn75
Fast solvent
HT - Si95
PREV:HT-Cr75 chromium additive
NEXT:HT - Ti75 titanium agent

go back

RELATED NEWS

Guess you're interested